Method for producing memory having a solid electrolyte material region

ABSTRACT

A method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell. A first material is formed in substantially pure form. A thermal treatment is carried out in the presence of at least one second material, and the chalcogenide material of the solid electrolyte material region thereby being produced.

CROSS-REFERENCE TO RELATED APPLICATIONS

This Utility Patent Application claims priority to German Patent Application No. DE 10 2004 029 436.4, filed on Jun. 18, 2004, which is incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to a method for producing a solid electrolyte material region and, in particular, to a method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell.

BACKGROUND

In the production of solid electrolyte memory cells, sputtering processes are used for forming the solid electrolyte material region that is to be provided as the memory. What is disadvantageous about these methods, however, is the inadequate reproducibility of the layer properties and also, in particular, the lack of layer homogeneity. Moreover, sputtering methods of this type exhibit difficulties with regard to satisfying ever more rigorous dimensioning requirements with regard to a maximum scale of integration to be achieved for corresponding memory elements and memory devices. Even the use of so-called CVD processes can only provide a remedy to a limited extent in this case because processes of this type are based on material combinations which are comparatively temperature-sensitive and can therefore lead to difficulties during the subsequent further processing processes.

For these and other reasons, there is a need for the present invention.

SUMMARY

A method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell. A first material is formed in substantially pure form. A thermal treatment is carried out in the presence of at least one second material, and the chalcogenide material of the solid electrolyte material region thereby being produced.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of the present invention and are incorporated in and constitute a part of this specification. The drawings illustrate the embodiments of the present invention and together with the description serve to explain the principles of the invention. Other embodiments of the present invention and many of the intended advantages of the present invention will be readily appreciated as they become better understood by reference to the following detailed description. The elements of the drawings are not necessarily to scale relative to each other. Like reference numerals designate corresponding similar parts.

FIGS. 1A-E are schematic and sectional side views of intermediate stages that are reached in one preferred embodiment of the method according to the invention for producing a solid electrolyte material region in a memory.

FIGS. 2A-E are schematic and sectional side views of intermediate stages that are reached in one preferred embodiment of a method according to the invention for producing a solid electrolyte material region in a memory.

FIGS. 3A-F are schematic and sectional side views of intermediate stages that are reached in one preferred embodiment of a method according to the invention for producing a solid electrolyte material region in a memory.

DETAILED DESCRIPTION

In the following Detailed Description, reference is made to the accompanying drawings, which form a part hereof, and in which is illustrated by way of illustration specific embodiments in which the invention may be practiced. In this regard, directional terminology, such as “top,” “bottom,” “front,” “back,” “leading,” “trailing,” etc., is used with reference to the orientation of the Figure(s) being described. Because components of embodiments of the present invention can be positioned in a number of different orientations, the directional terminology is used for purposes of illustration and is in no way limiting. It is to be understood that other embodiments may be utilized and structural or logical changes may be made without departing from the scope of the present invention. The following detailed description, therefore, is not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims.

The present invention provides a method for producing a solid electrolyte material region which can produce thin structures extended with small dimensioning in a particularly simple yet nevertheless reliable manner.

In one embodiment of a method according to the invention for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell, a solid electrolyte material region is formed from or with a chalcogenide material. In this embodiment, at least one first material region is formed from at least one first material on which the chalcogenide material is based, in a substantially pure form. A thermal treatment process is then carried out on the resulting structure or on the structure obtained, to be precise in the presence of at least one second material on which the chalcogenide material is based. The chalcogenide material of the solid electrolyte material region is produced in this case.

Consequently, a basic idea of the present invention is to produce the constituent required for the solid electrolyte material region from chalcogenide material by providing an underlying first material and then carrying out a thermal treatment step on the first material in the presence of a second underlying material, and thereby overall to carry out a conversion to form the required chalcogenide material of the solid electrolyte material region.

In one embodiment of a method according to the invention for producing a solid electrolyte material region, it is provided that the at least one second material on which the chalcogenide material is based or a part thereof is provided as a further material region or in a further material region.

As an alternative embodiment, it may be provided that the at least one second material on which the chalcogenide material is based or a part thereof is provided as a process atmosphere or in a process atmosphere.

The two possibilities of providing the at least one second material on which the chalcogenide material is based may also be combined with one another or be effected alternately with one another.

In accordance with a further additional or alternative embodiment of the method according to the invention, it is provided that the at least one second material on which the chalcogenide material is based or a part thereof is provided as a liquid or in a liquid.

In accordance with a further measure, it is provided that, as an alternative or in addition the thermal treatment or a part thereof is initiated thermally and/or carried out thermally. However, other possibilities of initiating and/or carrying out the thermal treatment are also conceivable.

By way of example, it may be provided that the thermal treatment or a part thereof is initiated and/or carried out thermally in the context of an irradiation using a laser or a laser beam, in particular in a local or localized manner.

In another alternative or additional embodiment of a method according to the invention for producing a solid electrolyte material region, it is provided that the thermal treatment step or a part thereof is carried out in the context of a furnace process and/or in the context of an RTA process.

In a further advantageous refinement of a method according to the invention for producing a solid electrolyte material region, it is provided that a plurality of layers of the at least one first and of the at least one second material on which the chalcogenide material is based are deposited progressively and/or alternately, and that the thermal treatment step is then effected, that is to say that the thermal treatment is carried out in particular on a stack of a sequence of the first and second materials for the chalcogenide material region.

In accordance with another embodiment of a method according to the invention, it may be provided that the at least one first material on which the chalcogenide material is based is or has a material from the group formed by germanium Ge, silicon Si, tungsten W and arbitrary mixtures or compounds thereof.

Furthermore, it may be provided as an alternative or in addition that the at least one second material on which the chalcogenide material is based on or has Se₂S₂O.

These and further aspects of the present invention are also explained in more detail on the basis of the elucidations below.

In one embodiment, the invention relates in particular inter alia to a method for producing thin GeSe and GeS chalcogenide layers by means of thermal methods.

The present notification of invention describes a method for producing thin chalcogenide layers, such as e.g. made of Ge_(x)Se_(1-x) and Ge_(x)S_(1-x) which may be used as solid electrolyte materials in semiconductor memory elements. By way of example, Si—Se or Si—S are also conceivable. Hitherto, various sputtering processes have been proposed as processes for depositing GeSe and GeS layers. However, these processes have the inherent disadvantage of not being suitable for bulk production for small lateral dimensions, in particular less than 100 nm, since the reproducibility and layer homogeneity of the processes are not good enough. See, for example, Journal of Non-Crystalline Solids (1991) vol. 130, no.1, p. 52-7. 21 refs. CODEN: JNCSBJ ISSN 0022-3093 Journal paper Broese, E.; Schroter, B.; Lehmann, A.; Richter, W.; Schirmer, G.; “Optical properties of quasi-simultaneous sputtered Ge_(x)Se_(1-x),”, Physics of Non-Crystalline Solids Taylor & Francis: London, UK, 1992. p. 193-7, xvi+761 pp., 7 refs. Conference: Cambridge, UK, 4-9 Aug. 1991 ISBN 0-7484-0050-8 Conference paper (English) Moore, M. W.; France, P. W.; Davey, S. T.; ed. Pye, L. D.; La Course, W. C.; Stevens, H. J. “Sputtering of chalcogenide coatings on to fluoride glass”. Added to this is the fact that the sputtering process is not suitable for filling very small contact holes since holes in the material, so-called “voids”, material “seams”, form on the undersides of the sidewalls, and reduce the functionality of the layers (to function as solid electrolyte material) or even render it totally unusable since the material properties at these weak points deviate significantly from those of the rest of the layer.

In order to produce thin Ge_(x)Se_(1-x) layers, only a PECVD deposition by using germanium (GeH₄) has been disclosed hitherto besides the sputtering methods mentioned. See, for example, E. Marquez et al., “On the optical constants of amorphous Ge_(x)Se_(1-x) thin films of non-uniform thickness prepared by plasma-enhanced chemical vapour deposition”, Vacuum 52 (1999) 55-60, V. Boev et al., “Holographic investigations of photoinduced changes in PECVD Ge—Se thin films”, Vacuum 47 (1996) 1211-1213. Through plasma CVD (PECVD), however, structural damage to the layer is to be expected as a result of the high energy of individual particles in the plasma.

One disadvantage of the CVD processes that use GeH₄ as germanium carrier gas is the fact that the GeH₄ is not suitable for thermal CVD of Ge_(x)Se_(1-x), and Ge_(x)S_(1-x) layers since the decomposition temperature of GeH₄ is very high. Combined Ge and Se CVD processes tends to be difficult to establish since they have to proceed at low temperatures in order to produce amorphous Ge—Se and/or Ge—S layers.

In the context of this invention, the electrolyte layer Ge_(x)Se_(1-x) or Ge_(x)S_(1-x) of the memory cell is formed in a two-stage process. This has the advantage that critical processes can be separated (deposition and thermal annealing). Since only pure (one-component) materials are deposited during the deposition, the advantage of increased purity and simplified process implementation and process control is afforded. Moreover, this process has the advantage that the GeSe or GeS layer can be formed in a self-aligned manner with respect to the contact hole.

In the case of a PMC cell, one targeted approach is to fill a contact hole with a chalcogenide material (e.g., by means of a CVD process). With CVD it is possible to fill narrow contact holes with unfavorable (high) aspect ratios. The CVD method proposed makes it possible to reproducibly produce extremely thin layers with sufficient edge coverage, so that the layers can be filled conformally even into narrow contact hole openings, which is necessary in the context of scaling of the lateral geometrical dimension. Further advantages of layers deposited by means of CVD are their layer homogeneity, density and purity. However, this notification of invention is not limited to layer deposition by means of CVD, rather it is likewise possible to use other deposition methods to deposit the initial layer(s).

By using a method that has not yet been utilised hitherto to successively deposit pure germanium and selenium (or sulfur) and to subsequently subject these individual layers and/or multilayers to heat treatment in a suitable atmosphere (possibly containing sulfur or selenium), it is possible to produce germanium selenide (Ge—Se) and germanium sulphide (Ge—S). A further possibility that is mentioned in this notification of invention is to expose a pure germanium layer to a suitable atmosphere containing selenium (or sulfur) in order thus to implement the Ge—Se or Ge—S layer growth process. Corresponding structures or processes with or comprising Si, Si—Se or Si—S are also conceivable.

Embodiment a) (FIGS. 1A to 1E)

Germanium is deposited (e.g. by means of CVD, ALD, sputtering, spin-on, spray-coating, PLD, or the like) and subjected to thermal aftertreatment (by means of a furnace process or RTA process) in a selenium-containing (or sulfur-containing) atmosphere, so that a Ge—Se layer or a Ge—S layer forms, depending on the duration and the temperature chosen, as a result of a selenium or sulfur diffusion into the geranium layer. Corresponding structures with or comprising Si, Si—Se or Si—S are also conceivable. The following formation specifications are conceivable: Ge(S)+Se(g)=>Ge_(x)Se_(1-x)(s) or Ge(s)+H₂Se(g)=>Ge_(x)Se_(1-x) (s)+H₂ or Ge(s)+S(g)=>Ge_(x)S_(1-x)(s) or Ge(s)+H₂S(g)=>Ge_(x)S_(1-x)(s)+H₂

In this embodiment, the sulfur S or the selenium Se may have been supplied both in elementary gas form (e.g., decomposed in an RF plasma) and in molecular gas form in combined carrier gases, i.e., H₂Se or H₂S. In general, an increase in the layer thickness is to be assumed as a result of the thermal aftertreatment; in this case, the layer thickness will increase proportionally to the quantity of incorporated sulfur (or selenium). Silicon Si may also be used here in each case instead of germanium Ge.

Embodiment b) (FIGS. 1A to 1E)

A germanium layer and a selenium layer (or sulfur layer) are deposited successively. A thermal aftertreatment by means of a furnace process or RTA method then takes place, by means of which an intermixing of the Ge and Se layers takes place. The overall stoichiometry can be adapted with deposition of the correct layer thicknesses of the respective element. Embodiments with Si instead of Ge and/or with S instead of Se are also conceivable.

Embodiment c) (FIGS. 3A to 3F)

A multilayer stack of a plurality of layers (alternately germanium and selenium layers) (that is to say Ge/Se/Ge/Se/ . . . or Ge/S/Ge/S/ . . . ), are deposited successively. The individual layers can subsequently react thermally with one another e.g. in an inert gas atmosphere or at atmosphere containing selenium (or sulfur). The stoichiometry of the final layer is achieved by adapting the thickness of the individual layers.

It is possible to demonstrate that a competitor has employed the invention since, in case of dispute, the process sequence used is apparent upon inspection. The fact that for example a CVD method has been used to deposit the GE layer can be demonstrated by way of the edge coverage in a contact hole and/or by way of residual gas contaminants in the layer.

Structurally similar, comparable or equivalent elements are designated by the same reference symbols below. A detailed description is not repeated on every occasion that they occur.

The sequence of FIGS. 1A-1E describes a first embodiment of the method according to the invention for producing a solid electrolyte material region 16, to be precise on the basis of schematic and sectional side views of intermediate stages that are reached when performing the method.

In FIG. 1A, firstly a basic material or substrate 20 having a surface region 20 a and on that a first or bottom electrode 14 having a surface region 14 a are formed and/or provided.

In the transition to the intermediate state illustrated in FIG. 1B, a first material region 16″ made of a first material 16-1 is then formed on the surface region 14 a of the first or bottom electrode 14, said first material 16-1 being fundamental for the chalcogenide layer to be formed or for the material region to be formed made from a chalcogenide material or comprising a chalcogenide material. A free surface 16 a″, 16-1 a arises in this case.

In the transition to the intermediate state illustrated in FIG. 1C, the structure from FIG. 1B is then exposed to a process gas atmosphere 30, which, as a constituent, has a second material 16-2 or comprises the latter, the second material 16-2 likewise being fundamental for the chalcogenide material to be formed. The first material 16-1 may for example be germanium and/or silicon, which is provided in solid form, whereas the second fundamental material 16-2 is then provided either as a compound or in elementary form in gaseous fashion, e.g., as selenium in gaseous form.

In the transition to the intermediate state illustrated in FIG. 1D, the formation of the material region 16 or solid electrolyte material region 16 then takes place, which is formed by the solid electrolyte material 16′, which, for its part, arises from a conversion of the first material 16-1 for the chalcogenide material 16 in the presence of the second material 16-2 for the chalcogenide material 16′, to be precise in the context of a thermal treatment. As has been described above, the thermal treatment may be thermally initiated and/or conducted; however, it may also be initiated and/or conducted on the basis of other sources of energy, e.g., on the basis of other types of electromagnetic radiation, on the basis of particle radiation, etc. The completion of the solid electrolyte material region 16 made of the solid electrolyte material 16′ or chalcogenide material 16′ then gives rise to the structure with a free surface region 16 a, 16 a′ illustrated in FIG. 1D.

In the transition to the intermediate state illustrated in FIG. 1E, a second or top electrode 18 having a surface region 18 a is then formed on the free surface 16 a, 16 a′ of the structure illustrated in FIG. 1D. In this way, a corresponding memory element 10 then results for the solid electrolyte memory cell 1.

The embodiment of the production method according to the invention for a solid electrolyte material region 16 in accordance with FIGS. 1A to 1E thus consists in providing a first fundamental material 16-1 in a solid-like manner on a surface region 14 a of the bottom electrode 14 and then offering the second fundamental material 16-2 in a gaseous manner as process gas atmosphere or as part of the process gas atmosphere in the context of the thermal treatment step.

The sequence of FIGS. 2A to 2E likewise show, in schematic and sectional side view, intermediate stages that are reached in another embodiment of the method according to the invention for producing a solid electrolyte material region. In this case, FIGS. 2A and 2B essentially correspond to FIGS. 1A and 1B.

FIG. 2A illustrates the initial structure on which this embodiment is based and which, moreover, essentially corresponds to the initial structure illustrated in FIG. 1A. In FIG. 2A, a basic material or substrate 20 having a surface region 20 a and on that a bottom electrode 14 having a surface region 14 a are formed and/or provided.

In the transition to the intermediate state illustrated in FIG. 2B, a material region 16″ made of a first material 16-1 is then formed on the surface region 14 a of the first or bottom electrode 14, said first material 16-1 being fundamental for the chalcogenide layer to be formed or for the material region to be formed made from a chalcogenide material or comprising a chalcogenide material. A free surface 16 a″, 16-1 a arises in this case.

In the transition to the intermediate state illustrated in FIG. 2C, a second material region 16′″ made of a second material 16-2 that is fundamental to the chalcogenide material, having a free surface 16 a′″, 16-2 a, is then formed on the free surface 16 a″, 16-1 a of the first material region 16″ that is fundamental for the chalcogenide material and is made of the first fundamental material 16-1. The first fundamental material 16-1 and the second fundamental material 16-2 for the chalcogenide material are thus present in close proximity and in intimate contact with one another in accordance with the structure illustrated in FIG. 2C.

In the transition to the intermediate stage illustrated in FIG. 2D, the thermal treatment step is then performed, the fundamental materials 16-1 and 16-2 provided then being converted to form the solid electrolyte material 16′ or chalcogenide material 16′ of the solid electrolyte material region 16 having a free surface region 16 a, 16 a′.

In the transition to the intermediate state illustrated in FIG. 2E, a second or top electrode 18 having a surface region 18 a is then formed on the free surface 16 a, 16 a′ of the structure illustrated in FIG. 2D. In this way, a corresponding memory element 10 then results for the solid electrolyte memory cell 1.

The embodiment of the method according to the invention for producing a solid electrolyte material region in accordance with the sequence of FIGS. 2A to 2E is thus based on the fact that the first material 16-1 that is fundamental for the chalcogenide material and the second material 16-2 that is fundamental for the chalcogenide material are formed as individual layers one after the other and in intimate contact with one another on the first or bottom electrode 14 and are thereby ready together in solid-like form during the thermal treatment step for conversion into the solid electrolyte material region 16.

The sequence of FIGS. 3A to 3F illustrates, once again in the form of schematic and sectional side views, intermediate stages of another embodiment of the method according to the invention for producing a solid electrolyte material region.

The starting point for this embodiment of the method according to the invention is the basic structure which is illustrated in FIG. 3A and which essentially corresponds to the basic structure of FIGS. 1A and 2A.

In FIG. 3A, firstly a basic material or substrate 20 having a surface region 20 a and on that a first or bottom electrode 14 having a surface region 14 a are formed and/or provided.

In the transition to the intermediate state illustrated in FIG. 3B, a structure is produced which essentially corresponds to the structure from FIGS. 1B and 2B. In the transition to the intermediate state illustrated in FIG. 3B, a first material region 16″ made of a first material 16-1 is then formed on the surface region 14 a of the first or bottom electrode 14, the first material 16-1 being fundamental for the chalcogenide layer to be formed or for the material region to be formed made from a chalcogenide material or comprising a chalcogenide material. A free surface 16 a″, 16-1 a arises in this case.

In the transition to the intermediate state illustrated in FIG. 3C, a structure is then produced which essentially corresponds to the structure from FIG. 2C. In the transition to the intermediate state illustrated in FIG. 3C, a second material region 16′″ made of a second material 16-2 that is fundamental to the chalcogenide material, having a free surface 16 a′″, 16-2 a, is then formed on the free surface 16 a″, 16-1 a of the first material region 16″ that is fundamental for the chalcogenide material and is made of the first fundamental material 16-1. The first fundamental material 16-1 and the second fundamental material 16-2 for the chalcogenide material are thus present in close proximity and in intimate contact with one another in accordance with the structure illustrated in FIG. 2C.

In the transition to the intermediate stage of this embodiment of the production method according to the invention as illustrated in FIG. 3D, the method steps mentioned in connection with FIGS. 3B and 3C are then repeated in the known order, thus giving rise to the structure illustrated in FIG. 3D, in the case of which material regions 16″ and 16′″ of the first fundamental material 16-1 and of the second fundamental material 16-2, respectively, alternate alternately, thus giving rise to a sequence of, for example, four layers that is formed on the free surface region 14 a of the first or bottom electrode 14 in this order. It goes without saying that it is conceivable, however, to choose a smaller number, e.g., 3, or a larger number, e.g., 5, 6, 7, . . . , for this layer sequence. Furthermore, it is also conceivable that not always the same material compositions are chosen for the individual layers, rather there is variation with regard to the fundamental materials or else their concentrations in the individual layers.

In the transition to the intermediate state illustrated in FIG. 3E, the thermal treatment step is then carried out, by means of which the sequence of the material layers made of the first fundamental material 16-1 and the second fundamental material 16-2 is converted into the solid electrolyte material region 16 comprising the solid electrolyte material 16′ or chalcogenide material 16′ and having a free surface 16 a, 16 a′.

In the transition to the intermediate state illustrated in FIG. 3F, a second or top electrode 18 having a surface region 18 a is then formed on the free surface 16 a, 16 a′ of the structure illustrated in FIG. 3D. In this way, a corresponding memory element 10 then results for the solid electrolyte memory cell 1.

Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations may be substituted for the specific embodiments illustrated and described without departing from the scope of the present invention. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this invention be limited only by the claims and the equivalents thereof. 

1. A method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell comprising: forming the solid electrolyte material region with a chalcogenide material; and producing the chalcogenide material by forming at least one first material region from at least one first material on which the chalcogenide material is based, in a substantially pure form, to provide a structure, and thermally treating the structure in the presence of at least one second material on which the chalcogenide material is based.
 2. The method of claim 1, comprising providing the at least one second material on which the chalcogenide material is based as a further material region.
 3. The method of claim 1, comprising providing the at least one second material on which the chalcogenide material is based as a process atmosphere.
 4. The method of claim 1, comprising providing the at least one second material on which the chalcogenide material is based as a liquid.
 5. The method of claim 1, comprising carrying out the thermal treatment thermally.
 6. The method of claim 1, comprising using a laser to carry out thermally the thermal treatment in the context of an irradiation.
 7. The method of claim 6, comprising using the laser in a localized manner.
 8. The method of claim 1, comprising carrying out the thermal treatment using a furnace process.
 9. The method of claim 1, comprising carrying out the thermal treatment using an RTA process.
 10. The method of claim 1, comprising: progressively depositing a plurality of layers of the at least one first and of the at least one second material on which the chalcogenide material is based progressively; and then carrying out the thermal treatment step.
 11. A method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell comprising: forming the solid electrolyte material region with a chalcogenide material; and producing the chalcogenide material by forming at least one first material region from at least one first material on which the chalcogenide material is based, in a substantially pure form, to provide a structure, and thermally treating the structure in the presence of at least one second material on which the chalcogenide material is based wherein the at least one first material on which the chalcogenide material is based includes a material from the group formed by germanium Ge, silicon Si, tungsten W and arbitrary mixtures or compounds thereof.
 12. The method of claim 11, comprising: providing the at least one second material on which the chalcogenide material is based as a further material region; using a laser to carry out thermally the thermal treatment in the context of an irradiation; and using the laser in a localized manner.
 13. A method for producing a solid electrolyte material region for a memory element of a solid electrolyte memory cell comprising: forming the solid electrolyte material region with a chalcogenide material; and producing the chalcogenide material by forming at least one first material region from at least one first material on which the chalcogenide material is based, in a substantially pure form, to provide a structure, and thermally treating the structure in the presence of at least one second material on which the chalcogenide material is based wherein the at least one second material on which the chalcogenide material is based includes Se₂S₂₀.
 14. A method for producing a memory cell comprising: producing a memory element having a solid electrolyte material region; forming the solid electrolyte material region with a chalcogenide material; and producing the chalcogenide material by forming at least one first material region from at least one first material on which the chalcogenide material is based, in a substantially pure form, to provide a structure, and thermally treating the structure in the presence of at least one second material on which the chalcogenide material is based.
 15. The method of claim 14, comprising providing the at least one second material on which the chalcogenide material is based as a further material region.
 16. The method of claim 14, comprising providing the at least one second material on which the chalcogenide material is based as a process atmosphere.
 17. The method of claim 16, comprising providing the at least one second material on which the chalcogenide material is based as a liquid.
 18. The method of claim 17, comprising carrying out the thermal treatment using an RTA process.
 19. The method of claim 17, comprising using a laser to carry out thermally the thermal treatment in the context of an irradiation.
 20. A method for producing a memory cell comprising: forming a solid electrolyte material region with a chalcogenide material; and producing the chalcogenide material via forming a first material means on which the chalcogenide material is based, in a substantially pure form, to provide a structure, and thermal treatment of the structure in the presence of a second material on which the chalcogenide material is based. 